STAINLESS STEEL 321

UNS S32100
ASTM A 240, A 479, A 276
 

321 Stainless is available in the following forms at Haohua Industry

Sheet
Plate
Bar
Pipe & Tube
Fittings (i.e. flanges, slip-ons, blinds, weld-necks, lapjoints, long welding necks, socket welds, elbows, tees, stub-ends, returns, caps, crosses, reducers, and pipe nipples)
Weld Wire

 

321 Stainless Steel OverviewStainless Steel 321 sheets

Stainless 321 is a heat resistant, titanium stabilized, austenitic alloy that's commonly used for service in the 1000°-1600°F temperature range. 321 stainless is primarily used in applications that involve continuous and intermittent service temperatures within the carbide precipitation range of 800°-1500°F. Type 321 is similar to type 304 stainless but with a titanium addition of at least five times the carbon content. This titanium addition reduces or prevents carbide precipitation during welding and in the 800°-1500°F service conditions. In order to provide optimum resistance to intergranular corrosion and to polythionic acid stress corrosion cracking in service temperatures at 1500°-1650°F an air cool may be used.

 

What are the characteristics of 321 Stainless?

Oxidation resistant to 1600°F
Stabilized against weld heat affected zone (HAZ) intergranular corrosion
Resists polythionic acid stress corrosion cracking
 

Stainless 321 Chemical Composition, %

 

Cr

Ni

Mo

Cu

Ti

C

MIN

17.0

9.0

-

-

5x(C+N)

-

MAX

19.0

12.0

0.75

0.75

0.70

0.08

 

Mn

Si

P

S

N

Fe

MIN

-

0.25

-

-

-

-

MAX

2.0

1.0

0.04

0.03

0.1

Bal

 

What applications might 321 Stainless Steel be used?

Aircraft piston engine manifolds and exhaust stacks
Expansion joints
Thermal oxidizers
Refinery equipment
High temperature chemical process equipment

 

Mechanical Properties
Average Elevated Temperature Tensile Properties


Temperature, °F

Ultimate Tensile Strength, ksi

.2% Yield Strength, ksi

68

84

38

400

62

20.5

600

62

18

800

62

17

1000

59.5

16.5

1200

45.5

16

1400

27.5

14

 

Welding Stainless Steel 321

321 Stainless is readily welded by all common methods including submerged arc. Appropriate weld fillers are most often specified as AWS E/ER 347 or E/ER 321.

This alloy is generally considered to have comparable weldability to 304 and 304L stainless with the main difference being the titanium addition which reduces or prevents carbide precipitation during welding.

 

*Note: The specifications noted including ASTM, ASME, or other applicable authorities are correct at the time of publication. Other specifications may apply for use of these materials in different applications.

Friendly link: Stainless coils tubing | Titanium Alloy steel pipes | U tubes | Finned tubes | Ferritic Stainless Steel Pipes | Duplex Stainless steel pipes | Austenitic stainless steel pipes | Nickel Alloy steel pipes |
JIANGSU HAOHUA INDUSTRY GROUP
Tel: 0086-512-58220050 Fax:0086-512-58810865 E-mail: sales@haopipe.com
Add: No.17,Southeastern Avenue, Economic Development Zone (South Area),Zhangjiagang City, Jiangsu Province, China.